Oil resistance PVC compound for Wire & Cable
Product Description
C6953XXX is a PVC compound product used in wire and cable applications. The formulation is designed for cable compound which give good oil resistance at high temperature properties suitable for flame retardant and low smoke PVC.
Typical Application
Product Characteristics
International Compliance
• Sheathing cable
• Good oil resistance at high temperature
• High limited oxygen index value
• Low smoke density
• IEC 60502 PVC - ST2
• CAT A
• High limited oxygen index value
• Low smoke density
• CAT A
Physical Properties
| Property | Test Method | Specification | Unit |
| Specific Gravity | ASTM D792 | 1.61 – 1.67 | - |
| Hardness ShoreA /10 sec | Hardness ShoreA /10 sec | 91 - 97 | - |
| Heat Stability ( at 1800C) | VTPC Method | Min. 300 | Minute |
| Volume Resistivity (250C) (x 10E13) | JIS K 6723 | Min. 1 | Ohm.cm |
| Tensile Strength | IEC 60811 -1 -1 | Min. 12.5 | MPa |
| Elongation at Break | IEC 60811 -1 -1 | Min. 150 | % |
Heat Aging test (100 oC, 168hrs) | |||
| Tensile Strength after Aging at 1000C x 168 hrs | IEC 60811 -1 -2 | Min. 12.5 |
MPa |
| Elongation at Break after Aging at 1000C x 168 hrs | IEC 60811 -1 -2 | Min. 150 | % |
| Retention of Tensile Strength after Aging at 1000C x 168 hrs | IEC 60811 -1 -2 | 75 -125 | % |
| Retention of Elongation at Break after Aging at 1000C x 168 hrs | IEC 60811 -1 -2 | 75 -125 | % |
| Loss of Mass Aging at 1000C x 168 hrs | IEC 60811 -3-2 | Max. 1.5 | mg/cm2 |
| Oil Aging test (70 oC, 4hrs) | |||
| Retention of Tensile Strength after aging at 700C x 4 hrs | IEC 60811 -1 -2 | Min. 80 | % |
| at 700C x 4 hrs IEC 60811 -1 -2 Min. 80 % Retention of Elongation at Break after Aging at 700C x 4hrs | IEC 60811 -1 -2 | Min. 80 | % |
| Limited Oxygen Index | ASTM D 2863 | Min. 40 | % |
| HCL Emission: PH (Acid Gas Emission: PH) | IEC 60754-1 |
Min. 2.4 | - |
| Smoke Density (Nonflaming mode) | ASTM E662 | Max. 110 | DMC |